ECOPOWER Classification Of Rosin Resin

Rosin glyceride

Rosin glyceride, English name glycerol ester of rosin , alias for ester gum, hydrogenated ester gum and glycerol tri-rosin ester. There is no clear chemical structural formula, the main component is abietic acid triglyceride, and a small amount of abietic acid diglyceride and monoglyceride, in the food industry can be used as a base material in gum candy, food flavors, processing aids..

Rosin pentaerythritol ester

Fragrant pentaerythritol ester has the characteristics of low acid value , high hardness and high melting point . It is used in hot-melt adhesives , pressure-melt adhesives, shoe adhesives, laminating adhesives, sealants, paints, paints, inks, etc. It can also be used in rubber and plastics. The modifier is widely used in products .

Maleic aicresin

This product is rosin and maleic anhydride addition reaction of glycerol and prepared to the irregular shape , a pale yellow transparent solid . Was dissolved in coal tar, esters, vegetable oils, turpentine, insoluble in alcohol . The a resin light color , light resistance and strong , not yellowed , and good compatibility nitrocellulose , a film prepared therefrom , high strength , dry smoothness .

Special resin for road marking paint

This resin product is specially produced for the application of road marking paint. The road marking paint formulated with this resin has the characteristics of pressure resistance, wear resistance, pollution resistance, moderate leveling and fast drying speed, and has yellow resistance. Good, anti-aging and other advantages, it is a resin specially used as a bonding agent for hot melt road marking paint.

ECOPOWER ROSIN ESTER DERIVATIVES PRODUCT LIST

Rosin Glycerol Ester	G-85	85-88	2-4	≤10	Clear	For ester glue phenolic resin paints (through polymerization with plant oils); widely used in glue industry as low cost enhancer for hot-melt, pressure-sensitive and other bonding agents.
	G-90	88-93	2-4	≤10	Clear
	G-90L	88-93	≤1	≤10	Clear
Rosin Pentaerythritol Ester	P-100 L	98-102	≤1	≤20	Clear	Widely used as a tackifier in adhesives industry. Mainly used in EVA hot melt adhesive, hot melt pressure sensitive adhesives, hot melt coating, ester gum, phenolic varnishes, bookbinding glue, carpenters glue, structural adhesive etc.
	P-100	98-102	2-4	≤20	Clear
	P-115	113-117	2-4	≤20	Clear
Resin for Hot Melt Road-Marking	R-95	93-97	2-4	≤20	Clear	Specially used as the link of traffic marking painting,which have good resistance to crushing, abrasion and smudge, appropriate leveling and fast drying. They also have good resistance to yellowing and ageing. It is suitable for all kinds of bitumen road surface and cement road surface.
	R-100	97-103	2-4	≤20	Clear
	R-105	103-107	2-4	≤20	Clear
Maleic Acid Resin	M-120	120±5 oC	2-4	≤30	Clear	used in paint and coating industries widely, for production of phenolic paints (through polymerization with platoils); improve hardness of paint films, gloss and rubbing property for Polyesters, Nitro and PU paints;as adhesive or binder for thermosol and road marking paints
	M-130	130±5 oC	2-4	≤30	Clear
	M-140	140±5 oC	4-8	≥160	Clear
Alcohol-Soluble Maleic Modified Rosin Esters	MA-130	130±5 oC	4-6	185±10	–	used in intaglio printing paper ink.Water-base ink
Disproportionated Rosin	Super Grade	≥75	20	≥155	–	with lighter color,good reactivity,liquid soap from Disproportionated Rosin is more clear and transparent.widely used in synthetic rubber,waterbased PSA,pigment.
Disproportionated Rosin	1ST Grade	≥75	40	≥155	–